Crystal |
Structure / Lattice Constant(A) |
M.P. oC |
Density g/cm3 |
Thermo-Expans x 10-6/K |
Dielectric constant |
Lattice Mismatch to YBCO |
Growth Tech & max. size |
---|
LSAT |
Cubic, a = 3.868 |
1840 |
6.74 |
10 |
22 |
0.82 % |
CZ. 2" |
LaAlO3 |
Rhombo. a = 3.790 c = 13. |
2100 |
6.51 |
9.2 |
24.5 |
2.8 % |
CZ 3" |
MgO |
Cubic, a = 4.21 |
2852 |
3.58 |
12.8 |
9.80 |
7.9 % |
Arc melt 2" |
NdCaAlO4 |
Tetrag. a = 3.685 c = 12.12 |
1850 |
5.56 |
12.0 |
19.5 |
5.5 % |
CZ 35 mm |
NdGaO3 |
Orthor. a = 5.43 b = 5.50 c = 7.71 |
1600 |
7.57 |
7.80 |
25 |
1.1 % |
CZ, 2" |
SrTiO3 |
Cubic, a = 3.905 |
2080 |
5.12 |
10.4 |
300 |
0.12 % |
vernuil 30 mm |
SrLaAlO4 |
Tetrag. a = 3.756 c = 12.63 |
1650 |
5.92 |
10.5 |
16.8 |
3.7 % |
CZ, 1" |
SrLaGaO4 |
Orthor. a = 5.176 b = 5.307 c = 7.355 |
1600 |
4.88 |
2 ~ 10 |
16 ~ 20 |
5.7 % |
CZ, 1" |
YSZ |
Cubic, a = 5.125 |
~ 2500 |
5.80 |
10.3 |
27 |
31 % |
Arc melt 2" |
|