Epitaxial YBCO HTS Thin Film on SrTiO3 substrate up to 30 mm in diameter
MTI Corp joins with several research institutes around the world, to finally make high Tc superconducting epitaxial thin film commercially available at an affordable price. MTI supplies high quality double side epitaxial thin film up to 3" diameter on LaAlO3, LSAT, Al2O3 and SrTiO3 single crystal substrate by a unique technology.
This will make YBCO thin film available at low cost. Researchers don't need to grow thin film any more, but concentrate their talent on HTSC film related devices, such as microwave filter for wireless and HTSC Squid.
Main Specifications of HTS Film
Epitaxial thin Film Composition
<100> YBCO
Film dimension
both for one side or double side film
YBCO / LaAlO3 10x10 mm ~ 3" dia.
YBCO / LSAT 10x10 mm ~ 2" dia.
YBCO / Al2O3 10x10 mm ~3" dia
YBCO / STO 10x10 mm ~ 1" dia.
Epitaxial FWHM
< 0.2 o
Critical Transition Temperature Tc
90 K+/-5%
Transition Temp. range ΔTc
< 0.5 K
Critical Current Jc
2~3 MA/cm2 @ 77K 0T
Surface Resistivity Rs
< 1 m Ohm @ 10 GHz, 77K, 0T
Thin film thickness
100 ~ 500 nm
Uniformity for 2" wafer
Thickness 300-400nm
Tc 86K- 90K
Jc 3 +/-0.5 MA/cm2 @ 80% wafer center.
Note: Must store the sample in dry box and vacuum oven , other wise Tc may be lower. Anealing sample at 500oC for < 30 minute may recover Tc
Package
Sealed in Vacuum in a plastic box and bag.
Note: YBCO is very sensitive to moisture, and must be stored in desiccator box.