| Modle | EQ-Die-25S |
| Height | 50 mm |
| Diameter | 62.5mm |
| Weight | 7.0 Lbs |
Whole set pressing die includes |
• One 1.0" Square core die made of hardened steel and highly polished with hardness
Rc 60 - 62.- • Ra 0.08μm highly polished steel
- • One steel sleeve for core die protection
- • Two pushing rods (They are 12 mm and 50 mm long separately) highly polished and perfectly
fitted into the die. - • Two steel support plates
- • One steel cylinder for releasing out the sample.
- • Max. pressure: 30 metric tons
|
Pressing die installation schematic |
|
Instruction |  
- • Please click the link below to see our demonstration video of using the pressing die with round
pressing core. The operation procedure of 1'' square pressing die is the same as the round
pressing die.
|
Attention
|
1. The difference between round and square die is that the square pressing core can only be
inserted into the die cavity in just one orientation. Once you received the die, please try different
direction until you can fully insert the pressing core.- 2. Due to manufacture process technology, the surface roughness of this square version is little
rough than round die.
|
Cautions |
• Please must always wear protection goggles during operation !!!- • The pressing die cannot be used for pressing powder with the particle size < 30 microns.
Small particles may slip into the gap between pushing rod and steel sleeve and cause
damages to the sleeve during the compression. Ball mill and sieve the powder and apply only
the 32~75 microns powder to the pressing die to avoid the damages. Please consider using
the 3'' Dia. Sieve Set No.200&450 Mesh to separate the 32~75 microns particles from the
powder clumps. Please clean the mold via ethanol after the completion of each experiment.
- • Please use alcohol to clean the pressing die every time before use and store it in a dry
place with antirust oil after the operation to avoid rusting on the surface, because all pressing
dies are made by high-stretched carbon steel for achieving high hardness to meet essential
requirements of making ceramic or metal samples. Otherwise, the pressing surface could
probably get scratched. - • To avoid damaging the die core and sleeve, we strongly recommend you use the professional
laboratory hydraulic presses which ensure the most even pressing interface and uniform - pressure force.
- • For pressing sticky metal powders such as Al, Mg, Zn, it is necessary to use dry or alcohol-
based tool lubricant to lubricate the die and sleeve set to reduce friction during the
compression. - • Do not press flammable, explosive materials.
|
Application Note |
You may consider using EQ-BNMR for easy mold releasing. Please click the picture to order.
|
Steps to make sample pellet |
• Mixing and grinding chemical powder by agate mortar or Ball Mill- • Calcine mixed the powder in a high temp furnace under suitable temperature
- • Crushing and Grinding calcined powder again by mortar or ball mill
- • Put calcined powder in to the die
- • Pressing sample by a pressing machine under suitable pressure
- • Take out pellet sample from die
- • Sintering the pellet under suitable temperature
- • Then, a new material sample is formed!
|