| Model | EQ-Die-120D |
| Height | 2 3/8" (60 mm) |
| Inside Diameter | 4 3/4" (120mm) |
| Outside Diameter | 5“ （ 127 mm ） |
| Net Weight | 86 Lbs |
| Shipping Weight | 115 Lbs |
| Shipping Dimensions | 40" x 25" x 25" |
Whole set pressing die
includes |
• Double layer structure 120mm dry pressing die- • One 120 mm ( 4.75" I.D ) die is included, made of hardened steel and highly polished with hardness
Rc 60 - 62 - • Ra 0.08μm highly polished steel
- • One stainless steel sleeve is in outside to protect die from cracking
- • Two pushing rods highly polished and perfectly fitted into die
- • Two steel support plates
- • One steel cylinder for releasing out the sample
- • Max Compressive Pressure: 694 metric tons
- • This die is designed for making 4" sputtering target
|
Instruction |
 
|
Cautions |
• Please must always wear protection goggles during operation !!!- • The pressing die cannot be used for pressing powder with the particle size < 30 microns. Small particles
may slip into the gap between pushing rod and steel sleeve and cause damages to the sleeve during the
compression. Ball mill and sieve the powder and apply only the 32~75 micron powder to the pressing die
to avoid the damages. Please consider using the 3'' Dia. Sieve Set No.200&450 Mesh to separate the
32~75 microns particles from the powder clumps. Please clean the mould via ethanol after the completion
of each experiment.
- • Please use alcohol to clean the pressing die every time before use and store it in a dry place with
antirust oil after the operation to avoid rusting on the surface, because all pressing dies are made by
high-stretched carbon steel for achieving high hardness to meet essential requirements of making
ceramic or metal samples. Otherwise, the pressing surface could probably get scratched. - • To avoid damaging the die core and sleeve, we strongly recommend you use the professional laboratory
hydraulic presses which ensure the most even pressing interface and uniform pressure force. - • For pressing sticky metal powders such as Al, Mg, Zn, it is necessary to use dry or alcohol-based tool
lubricant to lubricate the die and sleeve set to reduce friction during the compression. - • Do not press flammable, explosive materials.
|
Application Note |
• You may consider using EQ-BNMR for easy mold release. Please click the picture below to order.
-
|
Steps to make sample
pellet |
• Mixing and grinding chemical powder by agate mortar or Ball Mill- • Calcine mixed the powder in a high temp furnace under suitable temperature
- • Crushing and Grinding calcined powder again by mortar or ball mill
- • Put calcined powder into the die
- • Pressing sample by a pressing machine under suitable pressure
- • Take out pellet sample from die
- • Sintering the pellet under suitable temperature
- • Then, a new material sample is formed!ing Oven
|