| Material | Cr12MoV Alloy Tool Steel Max. Working Temp. 400C | ASSAB 17 Alloy High-Speed Steel Max. Working Temp. 200C |
| Hardness | HRC 60 - 62 | HRC 68 - 70 |
Die Size | - Diameter(D): Ø15, 16, 18, 20, 22, 25 mm
- Core Depth(N): 40 mm
- Outside Dimensions (L×H): Ø53 × 120 mm
| - Diameter(D): Ø7, 8, 9, 10, 11, 11.5, 12, 12.7, 13 mm
- Core Depth(N): 30 mm
- Outside Dimensions (L×H): Ø43 × 93 mm
|
Other Sizes | - 2 mm - 25 mm
- Please choose standard size as the picture left for quick delivery and lower cost
- Special size also is available upon request.
|
| Vacuum Port | Barbed, OD 7.2 mm ID 3 mm Length 18.4 mm |
| Vacuum Level | <0.5 Torr |
| Roughness Average (Ra) | 0.08 μm |
Maximum Load | - Please click the picture below to see the max. load for each size of the die
- Max. pressure less than 800 MPa is recommended
|
Installation schematic | - To avoid the risk of accidents and damage to the Pressing Die, please read these instructions carefully before installation and before using it for the first time.
- Must Read the manual especially the die installation schematic before the operation.
- The operator must wear protective goggles.
- Must have Hydraulic Pellet Press equipped with the Protection Cover, please click the pic-2 to order.
- You may order a vacuum pump separately for the dies ( click picture below right)
|
Cautions | - WARNING:
- DO NOT press flammable, corrosive, or explosive materials
- The operator must wear a protection goggle.
- Attention:
- Use ethanol to clean the pressing die before and after use every time
- Use anti-rust oil after the operation and store it in a dry place to avoid rusting.
- NO pressing powder with particle size LESS THAN 30 micron should be used. Small particles may slip into the gap between pushing rod and steel sleeve and cause damages to the sleeve during the compression.
- Ball mill or ground the powder to the size of 32~75 microns powder before pressing.
- Suggestions:
- Please use a professional laboratory hydraulic press to ensure the evenness of the pressing interface
- For pressing sticky metal powders, such as Al, Mg, Zn, please use dry or alcohol-based lubricants to reduce friction during the compression.
|
Instruction | |
Application Note | You may consider using EQ-BNMR for easy mold release. Please click the picture below to order. |
Steps to make sample pellet | - Mixing and grinding chemical powder by agate mortar or Ball Mill
- Calcine mixed the powder in a high temp furnace under suitable temperature
- Crushing and Grinding calcined powder again by mortar or ball mill
- Put calcined powder into the die
- Pressing sample by a pressing machine under suitable pressure
- Take out pellet sample from die
- Sintering the pellet under suitable temperature in Oven
- Then, a new material sample is formed!
|
| Warranty | - Pressing Dies are consumable products and are not covered by MTI's warranty.
|