Layers by Layer
| - Matte Ink Layer: 3.0 g /m^2 ± 0.5 g/m^2
- Biaxially Oriented Nylon (ONy); 6-Nylon: 15 um ± 10%
- Adhesive Layer (Carbon Black Mixed): 3.8 g/m^2 ± 1.5 g/m^2
- Mat Surface (Treatment Layer)
- Soft Aluminum Foil (ALM): 8021 or 8079; 35 um ± 10%
Glossy Surface (Treatment Layer)
Adhesive Resin Layer (PPa): Acid-modified PP;20 um ± 10%
Polypropylene (PP): 15 um ± 10% - Glossy Surface (Treatment Layer)
- Adhesive Resin Layer (PPa): Acid-modified PP;20 um ± 10%
- Polypropylene (PP): 15 um ± 10%
|
| Thickness | 91 μm ± 10% |
| Width and Length | DNP-ALF30: Width 120 mm ± 0.5 mm x Length 30m
DNP-ALF50: Width 400 mm ± 0.5 mm x Length 50m
DNP-ALF300: Width 400 mm ± 0.5 mm x Length 300m
|
| Heat Seal Strength | 30 N / 15 mm or more |
| Laminate Strength ONy / ALM | 3.0 N / 15 mm or more |
| Laminate Strength ALM / PP | 5.0 N / 15 mm or more |
| Electrolyte Resistance ALM / PP | 4.0 N / 15 mm or more
Dip Brazing 85°C, 24 hours |
| Surface quality | Mat finish |
| Fish Eye | 2mm or less in diameter (clear),1mm or less in diameter (colored) |
| Molding Depth | < 8.0mm |
| Electrical Insulating | Good |
| Hot Sealing Condition | 180-190°C |
| Moisture Vapor / O2 Transmission Rate | 200ppm / 5 years |
| Solvent Retention | Less than 5mg/m2 |
| Appearance | Within the sample of the limit |
Slip Factor
| CPP/CPP less than 1.0 |
| SDS | SDS for Aluminum
SDS for Carbon Black
|
Application Notes & Video
| Click the picture below to see the finished polymer Li-Ion battery made by the heated sealer
   |