EQ-Lib-Pre-NCA is the precursor of NCA ( Ni0.8Co0.15Al0.05(OH2 ) for DIY Li--NCA cathode powder for high capacity Li-Ion cathode at your own composition.
Note: You must mix the precusor with LiOH. H2O and calcine the mixed powder at 750- 790oC before use
Specification
Package |
200g/bottle in vacuumed bag |
Composition |
Ni0.8Co0.15Al0.05(OH)2 |
Confirguration |
Sphere |
Particle size distribution |
D10:5±0.5μm
D50:13-18μm
D90:30±0.5μm |
Specific surface area |
~1.5m2/g |
Tap Density |
≥1.8g/cm3 |
Water Content |
<500ppm |
PPH value |
≤11.2 |
Mian Element |
Required Content |
Real Content(%) |
Li |
0 |
0 |
Ni |
80±0.5 |
80.07 |
Co |
15±0.5 |
15.10 |
Mn |
5±0.5 |
4.77 |
Impurity |
Required(ppm) |
Typical(ppm) |
Ca |
<300 |
49.58 |
Cu |
<50 |
ND |
Fe |
<100 |
96.34 |
Cr |
<50 |
27.51 |
Mg |
<300 |
44.56 |
Na |
<500 |
119.85 |
S |
<2000 |
391.5 |
Zn |
<100 |
4.19 |
Al |
<100 |
29.98 |
Si |
<300 |
75.23 |
Zr |
<5000 |
390.0 |
Y |
<250 |
170.12 |
Note |
MTI does not manufacture this product, and only sell the small quantity to research for development for new generation battery. If you need a larger quantity or have the question for IP, we will forward your inquiry to the producer. |
Application Notes:
- Please click to see Procedure for Preparing Anode & Cathode Electrode Slurry.
- Please keep the powder in vacuum box to avoid moisture.
- Please bake the powder in a vacuum oven at 120 - 150 °C before making slurry and coating to ensure max. capacity.